Basic Info
Model NO.: PA6-NA-LGF30
Usage: General Plastics
Plastic Forming Method: Injection
Specifications: Granule
Glass Fiber Content: PA6 30LGF
Name 2: PA6
Gravity: 1.156
Flexural Modulus: 2124MPa
Trademark: LFT-G
Specification: ce, sgs
Material: Polyamide(Nylon 6.66)/PA
Plastic Properties After Heated: Thermoplastic Plastics
Color: White
Advantage: Direct Factory, Hi-Q, Favorable Price
Name: Polyamide (Nylon 6) PA6
Shape: 2.75mm*3.00mm
Authentication: SGS
Model Number: Virgin
Transport Package: 25kg/Bag
Origin: China
Product Description
Specifications
Nylon PA6 Pellets:
High softening temperature, heat resistance
Wear-resistance, self-lubricating,
UL, SGS, RoHS, FDA
Flame retardant PA6, Nylon Fiberglass reinforced, UL94-V0,Polyamide 6, mineral reinforced PA6, Anti-Static PA plastic pellets
Nylon, also named as Polyamide, with good properties of high mechanical strength, high softening temperature, heat resistance, low coefficient of friction, wear-resistance, self-lubricant, shock-absorbing and silencers, oil resistance. Fiber-reinforced PA can reduce water absorption, so that they can withstand high temperature and high humidity working conditions. With such a superior performance, polyamide compounded materials have replaced some metals as the structural material. It's widely used in electronic and electrical appliances, automobiles, machinery industries, aerospace, military weapons and other field.
PA has very high mechanical strength, high softening temperature, heat resistance, low coefficient of friction, wear-resistance, self-lubricating, shock-absorbing and silencers, oil resistance, fiber-reinforced can reduce water absorption, so that they can withstand high temperature and high humidity working conditions. With such a superior performance, polyamide compounded materials have replaced some of metals as the structural material. Widely used in electronic and electrical appliances, auto mobiles, machinery industries, aerospace, military weapons and other fields
PA6 & PA66 Products Series and Specification :
| Product Series | Type | Specification | Decription |
| PA in the Electronic & Electrical Fields | Ordinary Grade | 5010NH | Good Flowability Impact Resistance |
| 6010NH | |||
| Carbon-fiber Reinforced Grade | 50Cx | High Rigidity Anti-static Highly Conductivity ( x=3,4,5,6 etc ) | |
| 60Cx | |||
| Flame-retardant Filled Grade | 50MxF | Dimensional Stability (Finished Products ) Good Surface Effect ( x=3,4,5,6 etc ) | |
| 60MxF | |||
| 50GMxF-GN | ( x=3,4,5,6 etc ) | ||
| 60GMxF | Dimensional Stability (Finished Products ) Excellent Comprehensive Properties ( x=3,4,5,6 etc ) | ||
| Flame-retardant Grade | 50GxF | Glass-fiber Reinforced Excellent Mechanical Properties( x=3,4,5,6 etc ) | |
| 60GxF | |||
| 60GxF-GN | Halogen-free Glass-fiber Reinforced ( x=3,4,5,6 etc ) | ||
| 5010F | Halogen-free Good Flowability Good Electrical Properties | ||
| 6010F | |||
| PA in Sport Equipments Field | Super Tough Grade | ST5010 | Low Temperature Resistance Impact Resistance |
| ST6010 | |||
| Reinforced Grade | ST50Gx | Ultra-high Hardness Low Temperature Resistance ( x=3,4,5,6 etc ) | |
| ST60Gx | |||
| PA in Manufactured Articles of Daily Use | Reinforced Grade | 50Gx | High Rigidity High Modulus ( x=3,4,5,6 etc ) |
| 60Gx | |||
| 50Gx-LFT | Long Glass-fiber Reinforced Ultra-high Rigidity ( x=6,8,10 etc ) | ||
| 60Gx-LFT | |||
| 50Gx-WR | Good Wear Resistance Good Comprehensive Properties( x=3,4,5,6 etc ) | ||
| 60Gx-WR | |||
| PA in Automobile Cooling Water Chamer | Reinforced Grade | 60Gx-HR | Anti-hydrolysis Refrigerant Resistance ( x=5,6 etc ) |
| 60GM5-HR | 25% Mineral Glass-fiber Reinforced Dimensional Stability (Finished Products ) Anti-hydrolysis | ||
| 60Gx-CS | Blow-injection Grade High Toughness ( x=3,4 etc ) | ||
| PA in Internal and External Decorative Parts | Reinforced Grade | 50G6-AT | High Rigidity Good Surface Effect |
| 60G6-AT | |||
| 60GM5-AT | Mineral Glass-fiber Reinforced Dimensional Stability (Finished Products ) Good Comprehensive Properties | ||
| PA6/ABS Alloy | 5020 | High Impact Resistance Matt Surface Effect | |
| 5020Gx | Glass-fiber Reinforced High Toughnes ( x=2,3,4 etc ) | ||
| PA in Automobile Engine Components | Reinforced Grade | 50Gx-HS | High Rigidity High Temperature Resistance ( x=5,6,7 etc ) |
| 60Gx-HS | |||
| Mineral Filled Grade | 50M6 | 30% Mineral-fiber Filled Size Stability (Finished Products ) Good Surface Effect | |
| 60GxMy | Mineral & Glass-fiber Reinforced Warpage Resistance Good Surface Effect ( x=3,4,5,6 etc; y=3,4,5 etc ) |
Notice:1. In the glass-fiber reinforced products, the actual content of glass fiber=subscript No×5,e.g. the actual glass fiber content of 50G6F is 6×5=30%.
2. In the mineral-fiber reinforced products, the actual content of glass fiber=subscript No×5,e.g. the actual glass fiber content of 50M6F is 6×5=30%
| TEST ITEM | CONDITION | TEST METHOD | UNITS | TEST DATA | |||
| Density | / | ASTM D792 | g/cm3 | 1.19 | |||
| Filler content | 600°CBurning | / | % | / | |||
| Mechanical Behavior | Tensile strength | 23°C | ASTM D638 | Mpa | 75 | ||
| Elongation at break | 23°C | ASTM D638 | % | 6 | |||
| Tensile modulus | 23°C | ASTM D638 | Mpa | 3050 | |||
| Bending strength | 23°C | ASTM D790 | Mpa | 79 | |||
| Flexural Modulus | 23°C | ASTM D790 | Mpa | 3150 | |||
| Charpy notched impact strength | Dry/Wet withont fracture | ASTM D256 | KJ/M2 | 6.5 | |||
| Thermal Performance | Heat distortion temperature | 1.82Mpa | ASTM D648 | °C | 230 | ||
| Melting point DSC | / | ASTM D648 | °C | 255 | |||
| Item | PA66 (injection grade) | |
| fire resistance | 0.8 | mm |
| specific gravity | 1.15 | --- |
| Mold Shrinkage (1.6mm) | 0.8 | % |
| Mold Shrinkage(3.2mm) | 1.1 | % |
| tensile strength | 89.6 | Mpa |
| elongation at break | 14 | % |
| flexural modulus | 3450 | Mpa |
| IZOD notch impact strength | 43 | J/m |
| Melting point | 264 | oC |
Nature Glass Fiber Reinforced Polyamide PA6:
| Properties | Standard | Condition | Unit | Value |
| Physical Properties | ||||
| Specific Gravity | D792 | 23°C | g/cm3 | 1.17 |
| Mold Shrinkage | D955 | Cold mold, 48 hrs | % | 1.2-2.1 |
| Moisture Absorption | D570 | 23 °C; 50 % RH | % | ≤2.0 |
| Filler Content | D5630 | 800°C/2h | % | 0 |
| Mechanical Properties | ||||
| Tensile Strength | D638 | 50mm/min | Mpa | 76 |
| Elongation at Break | D638 | 50mm/min | % | ≥30 |
| Flexural Strength | D790 | 3mm/min | Mpa | 118 |
| Flexural Modulus | D790 | 3mm/min | Mpa | 2400 |
| Izod Impact, Notched | D256 | 23°C | J/m | 55 |
| Thermal Properties | ||||
| Melting Point | DSC | 23°C | °C | 223 |
| Heat Deflection Temperature | D648 | 1.8 Mpa | °C | 70 |
| GWFI | IEC 60695 | 1.6 mm | °C | 960 |
| GWIT | IEC 60335 | 1.6 mm | °C | 750 |
| Flammability | UL94 | 1.6 mm | V0 | |
| Electrical Properties | ||||
| Comparative Tracking Index | IEC 60112 | 23°C | V | 250 |
| Volume Resistivity | IEC 60093 | 23°C | ohm·cm | ≥1013 |
Flame retardant PA6, Nylon Fiberglass reinforced, UL94-V0,Polyamide 6, mineral reinforced PA6, Anti-Static PA plastic pellets Application:
Gear, Bearing, Mechanical Component , Household Electrical Components, Automobile Accessories, etc
Flame retardant PA6, Nylon Fiberglass reinforced, UL94-V0,Polyamide 6, mineral reinforced PA6, Anti-Static PA plastic pellets Characteristic:
The product is based on PA6, PA66 resin as basic, add glass fiber, efficient flame retardants and various additives, formed by twin-screw extrusion blending.
Its characteristics, high mechanical strength, modulus, abrasion resistance, dimension stability,long-term work at higher temperatures