Polyamide 66 Long Glass Fiber reinforced PA66
Product Details
|
●Product material:nylon 66 plastic raw material ●Shape:granules/pellets ●Length:6-25mm ●Advantage:thougher,stronger,lighter |
|
◆Higher fiber aspect ratio can provide more powerful performance. ◆The excellent stress transfer of long fibers increases toughness without increasing strength or stiffness. |
◆Long fiber is unidirectional continuous throughout pellet ◆Higher fiber aspect ratio results in more robust performance
|
Product Specification
| Item | Typical Value Unit | Test method |
| Specific Gravity | 1.71 g/cm³ | ASTM D-792 |
| Molding Shrinkage | 0.10 - 0.40 % | ASTM D-955(1/8 in (3.2 mm) section) |
| Tensile Strength | 262 MPa | ASTM D-638 |
| Tensile Modulus | 21374 MPa | ASTM D-638 |
| Tensile Elongation | 1.5 - 2.5 % | ASTM D-638 |
| Flexural Strength | 407 MPa | ASTM D-790 |
| Flexural Modulus | 19306 MPa | ASTM D-790 |
| Notched Izod Impact | 481 J/m | ASTM D-256 |
| Un-Notched Izod Impact | 249 ℃ | ASTM D-4812 |
| Deflection Temperature | HB @ 1.5 mm | ASTM D-648 |
|
Drying: Before processing should ensure that the water content below 0.1%. If the material is exposed to the air and stored, it is recommended to dehumidify at 80C for 4 to 8 hours. If granule PA66 LFT is stored in a closed container, it can be used directly after 3 hours of temperature equilibration.
|
||
Product Picture
Application Range
Packing & Shipping
LFT Certification
LFT Team
Welcome to wholesale the high quality granule PA66 LFT made in China from our factory. As one of the leading manufacturers and suppliers in China, we are equipped with advanced equipment and technology. Please be free to get the customized products from us.
Contact Information
Hot Tags: polyamide 66 long glass fiber reinforced PA66, China, manufacturers, suppliers, factory, buy, customized