LFT-G® LCF40-PA66-LFT BC04B Natural Grade Composite
40% Long Carbon Fiber reinforced Nylon66 (polyamide66) PA66 LCF40 Composite
Product name: ● LFT-G® -PA66-LCF40 Composite Plastic Granules
Product Model: ● LFT-G® PA66-NA-BC04B
Resin type: ● Polymer, Polypropylene
Fiber type : ● Long Carbon Fiber
Fiber content: ● 40%
Color ： ● black, nature color
material properties: ● Injection molding, good mechanical properties, high strength engineer plastic composite/compounds FOR Inject auto parts, home appliance parts, sport parts.
LFT-G® PA66 LCF40 is 40% long carbon fiber reinforced Nylon66 (PA66,polyamide66) polymer thermoplastic composite material.LFT-G® PA66 LCF40 material manufactured using a pultrusion process that melt impregnates the fiber with the matrix resin to maximize performance.Long carbon fibers offer high strength and stiffness, good resistance to impact and fatigue, etc. several advantages when used as a reinforcement material in composites.
LFT-G® PA66 LCF50-BC05B (TDS) Natural Grade Technical Data Sheet
Material Characteristic
| Physical | Typical Characteristic | Testing Standard | ||
|
Specific Gravity/Density |
1.33 g/cm³ |
ASTM D-792 |
||
|
Molding Shrinkage |
0.10 - 0.30 % |
ASTM D-944 (1/8 in (3.2 mm)section) |
||
|
Mechanical |
Typical Characteristic |
Testing Standard |
||
|
Tensile Strength |
287 MPa 284 MPa |
ISO 427 ASTM D-638 |
||
|
Tensile Modulus |
33963 MPa 33812 MPa |
ISO:427 ASTM D-638 |
||
|
Tensile Elongation |
0.4- 1.4% 0.4- 2.4% |
ISO:427 ASTM D-638 |
||
|
Flexural Strength |
392 MPa 390 MPa |
GB/T 9341 ASTM D-790 |
||
|
Flexural Modulus |
21918 MPa 21486 MPa |
GB/T 9341 ASTM D-790 |
||
|
Notched Izod Impact |
31 KJ/m2 284 J/m |
ISO:180 ASTM D-246 |
||
|
Notched Charpy Impact |
30 KJ/m2 |
ISO:179 |
||
|
|
Email:candyhu@lfrtplastic.com |
|||
Rev:09/03/2023
What's the benefits of PA66 LCF composite?
PA66 LCF40 composite offers high tensile and flexural strength, which makes it a suitable replacement for metal in many applications. It has a higher strength-to-weight ratio than aluminum and can be used in applications where weight reduction is critical. For example, in the automotive industry, PA66 LCF40 composite is used to replace metal parts, such as engine brackets and crankshaft covers, to reduce vehicle weight and improve fuel efficiency.
Another advantage of PA66 LCF40 composite is its ease of processing. It can be molded into various shapes and sizes using injection molding, compression molding, or resin transfer molding processes. This makes it suitable for the mass production of parts with complex geometries.
The applications of LFT PA66
PA66 LCF40 composite is an excellent solution for high-performance applications that require exceptional strength, durability, and resistance to impact, fatigue, and creep. It offers significant advantages over traditional materials such as metal and plastic, including superior stiffness, strength, and dimensional stability.As the demand for high-performance materials continues to rise, PA66 LCF40 composite is likely to play an increasingly important role in a wide range of applications.