Excellent Nylon/PA66 Long Carbon Fiber Strengthening Granules

Product Description

Technical Data Sheet (Take pa66 Long Carbon Fiber 40% for example)

Item	Typical Characteristic	Testing Standard
Specific Gravity	1.31	ASTM D-792
Tensile strength	297 MPa	ASTM D-638
Tensile modulus	31034MPa	ASTM D-638
Tensile elongation	1.0-2.0%	ASTM D-638
Flexural Strength	455MPa	ASTM D-790
Flexural Modulus	20690MPa	ASTM D-790
Notched lzod Impact	214J/m	ASTM D-256
Un-Notched lzod Impact	801J/m	ASTM D-4812
Flame Retardant	HB@1.5mm	ASTM D-635
Deflection Temperature(1820kpa)	252°C	ASTM D-648

PA66 polyamide 66 or nylon 66 chemical and physical properties PA66 has a high melting point in polyamide materials.It's a semi-crystalline material.PA66 maintains high strength and stiffness at higher temperatures.

Our pa66 long carbon fiber reinforced thermoplastic is made to virgin excellent PA66 resin filled from 20-6o% content long carbon fiber.Due to the modified or strengthen way, under the original excellent characteristics, the hardness, creep resistance and stability of PA66 are further enhanced.Therefore, the reinforced has high toughness,light weight,high strength,wear resistance,corrossion resistance,creep resistance,conduction,heat transfer.

Application: Under the superior character,pa66 long carbon fiber strengthening granules could be suitable for wing of the aircraft,duck wing.stable wing,nacelle and other aerospace fields.The detail application of life has easy to be found .If you are interested in our product ,please contact us to know more product details.

Prouduct Process

Long carbon fiber reinforced thermoplastic material from resin bottom melt at high temperature after adding carbon fiber composite molding particles after cooling to cut grain;Then send to the laboratory, set the appropriate temperature and time for baking;After baking, the particles are made into test strips and sent to the laboratory for testing to check the tensileˎ impact ˎdensity and so on.

工艺流程

FAQ

1.What is difference between the Long carbon fiber PA66 pellets and the long carbon fiber PA66?

Long carbon fiber nylon66 pellets is made from one monomer which has 6 carbon atoms while Long carbon fiber PA66 pellets is made from 2 monomers with each one having 6 carbon atoms, hence the PA66 name. An important difference between Long carbon fiber nylon 6 pellets& 66 is mold shrinkage. PA66 would be a better choice between the two.

2.What is long carbon fiber nylon？What are the categories？

Long carbon fiber nylon is made by filling nylon with carbon fiber with different content.The Carbon fiber content is from 20%-60%.Different content of long carbon fiber has different characteristics.the higher content of carbon fiber,the better the characteristic.

Why Choose US

1.Possess own factories , can provide 100% factory price.
2.Our team has 20 years of comprehensive knowledge.
3.Advanced production equipment.
4.Good quality and good service.

Contact email: sale03@lfrtplastic.com

Contact whatsapp: +86 15727645397

Packing and Delivery

Sample: free ,but freight charged on customers

Delivery Time: 7-15days

Delivery Method: by sea , by air, by express

PA66 long carbon fiber