Pa6 LGF60 glass fiber content is higher, the better the performance, but more than 50% glass fiber content, the increase in performance is not obvious, compared with PA6 50% glass fiber content, 60% content in the process of higher requirements, our company in continuous experiments and production, to ensure that in the impregnation process to let the resin completely wrapped in the fiber,Reduce the floating fiber and running fiber, maximize the performance of PA6 LGF60.

In most cases, PA6 resin and glass fiber are mixed and processed in a ratio of 2:3 of the total weight, and the content of PA6 LGF60 produced will vary by 0.1-0.3 error.

LFT glass fiber fill nylon6

NO.	Item	Unit	Typical Characteristic	Testing Standard
	Nylon 6 LGF60 Polyamide Reinforced Thermoplastic 60%
1	Density	g/cm³	1.68	ASTM D-792
2	Molding Shrinkage	%	0.1-0.3	ASTM D-955
3	Tensile Strength	MPa	237	ASTM D-638
4	Tensile Modulus	MPa	23125	ASTM D-638
5	Tensile Elongation	%	1.5	ASTM D-638
6	Flexural Strength	MPa	333	ASTM D-790
7	Flexural Modulus	MPa	18864	ASTM D-790
8	Notched Izod Impact	J/m	316	ASTM D-256
9	Beam breach impact strength	J/M		ASTM D-4812

Xiamen LFT composite plastic Co., Ltd. is a high-tech enterprise specializing in the development and operation of polymer materials industry.Focus on the production of engineering plastics and special engineering plastics, widely used in high-speed rail, aviation, electrical appliances, automobiles, electronics and other industries.For the fundamental purpose of reducing the weight of structural performance components, the long fiber reinforced modification is developed into an economical and functional plastic instead of metal.Reduce the investment risk of customers, for customers to bring greater benefits.