PA6 LGF30 Composite | High-Performance Nylon 6 Composite | LFT-G®
PA6 LGF30: Advanced Long Glass Fiber Reinforced Nylon 6
PA6 LGF30 is an engineering-grade thermoplastic composite containing 30% long glass fiber reinforcement, developed to bridge the gap between traditional polymers and metal alloys. With a tensile strength of 165-175 MPa (ISO 527-2) and heat deflection temperature of 210°C (ISO 75), this material achieves 40% higher impact resistance than short-fiber equivalents while maintaining exceptional processability.
Key Technical Properties
1. Mechanical Performance
- Tensile Strength: 165–177 MPa (ISO 527-2), outperforming PA6 GF15 by 35-40%
- Flexural Modulus: 6800–8600 MPa (ISO 178), ideal for structural load-bearing
2. Thermal Properties
- HDT @1.8MPa: 207–215°C (ASTM D648)
- Continuous Use Temp: 130°C (IEC 60216)
3. Processing Advantages
- Melt Flow Index: 35–55 g/10 min (ISO 1133)
- Shrinkage Rate: 0.2–0.6% (ISO 294-4)
Competitive Advantages
1. Metal Replacement Solution
Delivers 60% weight reduction vs aluminum with equivalent structural rigidity, reducing CO₂ emissions in transportation applications.
2. Fatigue Resistance
Endures over 1×10⁷ cycles at 70 MPa stress (ASTM D671), suitable for engine mounts and suspension components.
Industrial Applications
Automotive Systems
- EV battery housings (UL94 V0 compliant)
- Transmission valve bodies
| Industry | Components | Benefit |
|---|---|---|
| Industrial | Conveyor chain guides | Wear resistance |
| Electronics | 5G antenna housings | Low dielectric loss |
Technical Specifications
| Property | Test Standard | Value |
|---|---|---|
| Density | ISO 1183 | 1.34 g/cm³ |
| Tensile Strength | ISO 527-2 | 185 MPa |
| Notched Charpy Impact | ISO 179/e | 28KJ/m2 |
| Flexural Modulus | ASTM D790 | 8300Mpa |
| HDT (1.8MPa) | ISO 75 | 210°C |
Download Data Sheet PDF
Hot Tags: lft-g® pa6 lgf30: advanced long glass fiber reinforced nylon 6, China, manufacturers, suppliers, factory, buy, customized