40% Long carbon Fiber reinforced Polyamide 66/6I
LFT-G® PA66-LCF40% Natural Grade Technical Data Sheet (TDS)
LFT-G® LCF40%-PA66-Natural Grade
Product name: LFT-G® LCF40%-PA66/6I Long Carbon Fiber Reinforced nylon6
Product Model: ● LFT-G® PA66/6I-INA-BC04
Product Length: ● 5-25 mm. General length 10-12 mm.
Resin type: ●Polyamide
Fiber type : ● Long carbon Fiber
Fiber content: ● 40%
Color ： ● black, nature color
material properties: ● Injection molding, natural grade, good mechanical properties, high load modulus Plastic composite.
LFT-G® LCF40%-PA66/6I material is 40% long carbon fiber reinforced nylon6 (PA6) thermoplastic composite manufactured using a pultrusion process that melt impregnates the fiber with the matrix resin to maximize performance.
LFT-G® PA66/6I-LCF40 is a type of composite material made from a blend of polyamide 66, polyamide 6I, and long carbon fiber. The composite has a 40% long carbon fiber content, which provides it with high strength and stiffness while maintaining good impact resistance. It is commonly used in applications that require high mechanical performance, such as automotive and aerospace industries.
Material Characteristic
| Physical | Typical Characteristic | Testing Standard | ||
|
Specific Gravity/Density |
1.32 g/cm³ |
ASTM D-792 |
||
|
Molding Shrinkage |
0.10 - 0.20 % |
ASTM D-955 (1/8 in (3.2 mm)section) |
||
|
Mechanical |
Typical Characteristic |
Testing Standard |
||
|
Tensile Strength |
305 MPa 303 MPa |
ISO 527 ASTM D-638 |
||
|
Tensile Modulus |
34335 MPa 34023 MPa |
ISO:527 ASTM D-638 |
||
|
Tensile Elongation |
0.6- 1.5% 0.6- 1.5% |
ISO:527 ASTM D-638 |
||
|
Flexural Strength |
433 MPa 430 MPa |
GB/T 9341 ASTM D-790 |
||
|
Flexural Modulus |
24335 MPa 24255 MPa |
GB/T 9341 ASTM D-790 |
||
|
Notched Izod Impact |
35 KJ/m2 293 J/m |
ISO:180 ASTM D-256 |
||
|
Notched Charpy Impact |
31 KJ/m2 |
ISO:179 |
||
|
Revised: 09/10/2021 www.lfrt-plastic.com |
Email:candyhu@lfrtplastic.com |
|||
What's the characters nylon66/6I material?
Nylon66/6I is a blend of polyamide 66 and polyamide 6I, which offers several desirable characteristics such as:
- High strength and stiffness: The combination of the two polymers provides a balance of strength and stiffness, making it suitable for applications that require high mechanical performance.
- Good chemical resistance: Nylon66/6I is resistant to oils, fuels, and many chemicals, making it suitable for use in harsh environments.
- High-temperature resistance: The material can withstand high temperatures without degrading, making it suitable for use in high-temperature applications.
- Good dimensional stability: Nylon66/6I has low moisture absorption and good dimensional stability, which makes it ideal for applications that require tight tolerances.
- Good surface finish: The material has a smooth surface finish, which makes it ideal for applications that require a high-quality appearance.
What is the advantage of long carbon fiber nylon ?
Thermoplastics with long carbon fibers use nylon PA6 resin. It is simple to produce, has excellent dielectric qualities, strong heat and chemical resistance, mechanical strength, and stiffness. It also has low friction and wear resistance.
What's applications of long carbon fiber nylon?
In the recent year, the most common application of long carbon fiber PA66 composite is in the automotive industry. It is used to manufacture lightweight and strong components such as structural parts, underbody shields, and battery modules. This composite material offers excellent strength-to-weight ratio, impact resistance, and fatigue endurance, which makes it ideal for automotive applications. Additionally, it helps to reduce the weight of vehicles, which in turn improves fuel efficiency and reduces carbon emissions.Long fiber nylon PA resins are thermoplastics that are partly crystalline and offer the perfect blend of qualities for automotive, furniture, medical, and electrical applications.