40% Long carbon Fiber reinforced Polyamide 6 LFT-G® PA6-LCF40% Natural Grade Technical Data Sheet (TDS)
LFT-G® LCF40%-PA6-Natural Grade
Product name: LFT-G® LCF40%-PA6 Long Carbon Fiber Reinforced nylon6
Product Model: ● LFT-G® PA-NA-BC04
Product Length: ● 5-25 mm. General length 10-12 mm.
Resin type: ●Polyamide
Fiber type : ● Long carbon Fiber
Fiber content: ● 40%
Color ： ● black, nature color
material properties: ● Injection molding, natural grade, good mechanical properties, high load modulus Plastic composite.
LFT-G® LCF40%-PA6 material is 40% long carbon fiber reinforced nylon6 (PA6) thermoplastic composite manufactured using a pultrusion process that melt impregnates the fiber with the matrix resin to maximize performance.
LFT-G® PA6-LCF40 is a specific type of Polyamide 6 Long Carbon Fiber composite material that contains 40% by weight of long carbon fibers. This LFT-G® PA6-LCF40 composite material has higher stiffness and strength compared to PA6 carbon fiber with lower fiber content, making it suitable for more demanding applications where high performance is required.
Material Characteristic
| Physical | Typical Characteristic | Testing Standard | ||
|
Specific Gravity/Density |
1.32 g/cm³ |
ASTM D-792 |
||
|
Molding Shrinkage |
0.10 - 0.30 % |
ASTM D-955 (1/8 in (3.2 mm)section) |
||
|
Mechanical |
Typical Characteristic |
Testing Standard |
||
|
Tensile Strength |
287 MPa 279 MPa |
ISO 527 ASTM D-638 |
||
|
Tensile Modulus |
44670 MPa 47804 MPa |
ISO:527 ASTM D-638 |
||
|
Tensile Elongation |
0.5- 1.5% 0.5- 1.5% |
ISO:527 ASTM D-638 |
||
|
Flexural Strength |
392 MPa 373 MPa |
GB/T 9341 ASTM D-790 |
||
|
Flexural Modulus |
20282 MPa 21310 MPa |
GB/T 9341 ASTM D-790 |
||
|
Notched Izod Impact |
37 KJ/m2 241 J/m |
ISO:180 ASTM D-256 |
||
|
Notched Charpy Impact |
KJ/m2 |
ISO:179 |
||
|
Revised: 1/11/2019 www.lfrt-plastic.com |
Email:candyhu@lfrtplastic.com |
|||
What is the advantage of long carbon fiber nylon ?
Long carbon fiber nylon6 composites offer several advantages (High strength and stiffness, Lightweight, Corrosion resistance, design flexibility, Cost-effective) than traditional materials such as metals, short fiber composites, and unreinforced plastics.
Long carbon fiber nylon composites offer several advantages over short carbon fiber nylon composites, including:
- Higher strength and stiffness: Long carbon fibers provide better reinforcement and result in higher strength and stiffness compared to short carbon fibers.
- Improved fatigue resistance: Long carbon fibers provide better resistance to cyclic loading and fatigue compared to short carbon fibers.
- Reduced warpage: Long carbon fibers have a lower aspect ratio, which reduces the likelihood of warpage during processing.
- Improved impact resistance: Long carbon fiber nylon composites exhibit improved impact resistance compared to short carbon fiber nylon composites.
- Better dimensional stability: Long carbon fiber nylon composites exhibit better dimensional stability over a wide range of temperatures and humidity levels compared to short carbon fiber nylon composites.
What's applications of long carbon fiber nylon?
Long carbon fiber nylon composites are used in various applications across industries such as automotive, aerospace, sporting goods, electronics, and industrial equipment due to their high strength, stiffness, lightweight, and corrosion-resistant properties.
Why choose Us
- Full scale of customized material and color matching service
- THE most suitable，precise and alternative material solutions suggestion
- costing down,the most competitive price based on good and suitable quality
- Quickest delivery period according to customers requirement
Contact us
Hot Tags: lft-g® lcf40%-pa6, China, manufacturers, suppliers, factory, buy, customized