Polyamide Nylon PA6 composite Pellets is a 30% -60% long glass fiber reinforced nylon 6 (polyamide 6) thermoplastic composite manufactured using a pultrusion process that melt impregnates the fiber with the matrix resin to maximize performance. Long glass fiber reinforcement provides this composite with increased stiffness, strength, and durability.

This composite’s mechanical properties allow its use in a wide range of applications across multiple market segments as a lightweight replacement for metals or as an engineered substitute for other materials.

Polyamide Nylon PA6 composite Pellets Physical	Polyamide Nylon PA6 composite Pellets Typical Characteristic	Polyamide Nylon PA6 composite Pellets Testing Standard
Specific Gravity	1.56 g/cm³	ASTM D-792
Molding Shrinkage	0.10 - 0.30 %	ASTM D-955
Tensile Strength	226 MPa	ASTM D-638
Tensile Modulus	17935 MPa	ASTM D-638