Xiamen LFT Composite Plastic
Technical Data Sheet
LFT-G® PP-NA-LGF20
|
Product name |
● LFT-G®PP-NA-LGF20 |
|
|
Polymer Matri |
● PP (Polypropylene) |
|
|
Fiber Type |
● Long glass fiber |
|
|
Fiber Content |
● 20% |
|
|
Color |
● Natural, and custom colors |
|
|
Processed method |
● Injection molding |
| Physical | Typical Characteristic | Testing Standard |
 |
||
|
Specific Gravity |
1.03 g/cm³ | ASTM D-792 |
|
Molding Shrinkage |
0.20 - 0.40 % |
ASTM D-955(1/8 in (3.2 mm)section) |
| Mechanical | Typical Characteristic | Testing Standard |
 |
||
|
Tensile Strength |
110 MPa | ASTM D-638 |
|
Tensile Modulus |
5406 MPa | ASTM D-638 |
|
Tensile Elongation |
2.2 - 3.3 % | ASTM D-638 |
|
Flexural Strength |
133 MPa | ASTM D-790 |
|
Flexural Modulus |
3945 MPa | ASTM D-790 |
|
Notched Izod Impact |
255 J/m | ASTM D-256 |
|
Un-Notched Izod Impact |
753 J/m | ASTM D-4812 |
| Thermal | Typical Characteristic | Testing Standard |
 |
||
|
Deflection Temperature @ 264 psi (1820 kPa) |
146 ℃ | ASTM D-648 |
| Flammability | Typical Characteristic | Testing Standard |
 |
||
|
Flame Retardant |
HB @ 1.5 mm | ASTM D-635 |
| Injection | Typical Characteristic |
 |
|
|
Injection Pressure |
69 - 103 MPa |
|
Melt Temperature |
210 - 280 ℃ |
|
Mould temperature |
25 - 80 ℃ |
|
Pre-drying |
4 hrs @ 82 ℃ |
|
Moisture Content |
0.02 % |
Processing Notes
Molding guidelines and processing conditions for LFT-G® long fiber composite pellets are available in our Material Processing Guide. Please contact our technical support team if you require additional information regarding processing a particular product or guidance resolving problems.
Values included in this Property Data Sheet are based on limited laboratory test specimens. These values are typical values and are not meant to be used for setting maximum or minimum values for specification purposes. Any determination of the suitability of the materials shown in this property data sheet for use by the end user is the sole responsibility of the user, who must assure himself that the material as subsequently processed meets the need of his particular product or use. To the best of our knowledge the information in this publication is accurate and reliable, LFT-G® does not assume any liability whatsoever for the accuracy of this information.